Autoclaved aerated concrete is a kind of wall material with many advantages, such as heat preservation, fire prevention, sound insulation, moisture-proof, environmental protection，recycled using etc. The AAC products with porous structure are lighter, and easier to cut, drill and construct which saves the labour cost.
We are specialized in providing services for the whole plant solution of autoclaved aerated concrete, including raw material testing, plant planning, customized equipment design, equipment manufacturing, pre delivery inspection, supervision of project site installation and personnel training.
Autoclaved aerated concrete is a kind of wall material with many advantages, such as heat preservation, fire prevention, sound insulation, moisture-proof, environmental protection，recycled using etc. The AAC products with porous structure are lighter, and easier to cut, drill and construct which saves the labour cost.
We are specialized in providing services for the whole plant solution of autoclaved aerated concrete, including raw material testing, plant planning, customized equipment design, equipment manufacturing, pre delivery inspection, supervision of project site installation and personnel training.
| Process | Parameter |
| Mixing period | 5-6 minutes |
| Pouring slurry temperature | 40-45 C |
| Cake curing time | 2.5-3.0h |
| Cake curing temperature | 45~55 C |
| Cake strength after curing | 0.15~0.18MPa |
| Autoclaved curing system Before-after autoclave | 0.5h |
| Vacuumize | 0.5h(0 ~ -0.06MPa) |
| Listing pressure | 1.5h(-0.06~1.3MPa) |
| Constant pressure | 8h(1.3MPa) |
| Releasing pressure | 1.5h(1.3~0MPa) |
| total | 12h |
| Process | Parameter |
| Mixing period | 5-6 minutes |
| Pouring slurry temperature | 40-45 C |
| Cake curing time | 2.5-3.0h |
| Cake curing temperature | 45~55 C |
| Cake strength after curing | 0.15~0.18MPa |
| Autoclaved curing system Before-after autoclave | 0.5h |
| Vacuumize | 0.5h(0 ~ -0.06MPa) |
| Listing pressure | 1.5h(-0.06~1.3MPa) |
| Constant pressure | 8h(1.3MPa) |
| Releasing pressure | 1.5h(1.3~0MPa) |
| total | 12h |
Raw Materials:
Siliceous materials : Sand / Fly ash / Tailings containing silicon / Ceramic waste
Calcareous material: Lime block + cement + gypsum
Others: Aluminum powder paste
Cement technical requirements as blow:
(1) Free CaO content should be not more than 1.5%, CaO content is 60%.
(2) NaCl & KCl content should be not more than1%~1.5%.
(3) Specific surface area 2500~3500cm3/g.
(4) Volume stability is qualified.
(5) Setting time initial setting 1~3h final setting 3~6h.
Main technical index for sand:
| Name Grade | SiO2% | K2O+Na2O% | Organic matter | Mica% | SO3% | Mud% | Moisture content% |
| High-class | 85 | 1 | Qualified | 0.5 | 1 | 3 | 8 |
| Firs-class | 75 | 3 | 5 | ||||
| Qualified product | 65 | 5 | 1 | 2 | 8 |
Grain composition for sand:
| Name Grade | Content,% | ||
| High-class | First-class | Qualified product | |
| 2.5～5.0(round hole) | 0 | 0 | |
| 1.25～2.5(square hole) | 10 | 10 | |
| 0.16～0.25(square hole) | 60 | 45 | |
| ＜0.16(square hole) | 30 | 45 | |
Lime :
Lime is also one of the main raw material. Its function is coordinating with cement to provide effective calcium oxide, than makes it working with SiO2, Al2O3 from silica material under hydrothermal condition to generate hydrated calcium silicate. Effective calcium oxide content should be more than 65%, the best is more than 80%.
Aluminum paste ( powder):
Aluminum paste is according to JC/T 407 Aluminum Paste for AAC standard. Aluminum powder should be according to the current national standard.
Gypsum:
The regulating effect of gypsum mainly reflects in deferring the speed of quick lime digesting & slurry thickening.
Water:
According to the standard, water ratio is advisable to 0.60.
Water quality requirement
| Content | pH | Cl- (mg/L) | SO42-(mg/L) | Na+ +K+(mg/L) | K+ (mg/L) |
| Operating range | 6~9 | ＜600 | ＜1000 | ＜450 | ＜100 |
Raw Materials:
Siliceous materials : Sand / Fly ash / Tailings containing silicon / Ceramic waste
Calcareous material: Lime block + cement + gypsum
Others: Aluminum powder paste
Cement technical requirements as blow:
(1) Free CaO content should be not more than 1.5%, CaO content is 60%.
(2) NaCl & KCl content should be not more than1%~1.5%.
(3) Specific surface area 2500~3500cm3/g.
(4) Volume stability is qualified.
(5) Setting time initial setting 1~3h final setting 3~6h.
Main technical index for sand:
| Name Grade | SiO2% | K2O+Na2O% | Organic matter | Mica% | SO3% | Mud% | Moisture content% |
| High-class | 85 | 1 | Qualified | 0.5 | 1 | 3 | 8 |
| Firs-class | 75 | 3 | 5 | ||||
| Qualified product | 65 | 5 | 1 | 2 | 8 |
Grain composition for sand:
| Name Grade | Content,% | ||
| High-class | First-class | Qualified product | |
| 2.5～5.0(round hole) | 0 | 0 | |
| 1.25～2.5(square hole) | 10 | 10 | |
| 0.16～0.25(square hole) | 60 | 45 | |
| ＜0.16(square hole) | 30 | 45 | |
Lime :
Lime is also one of the main raw material. Its function is coordinating with cement to provide effective calcium oxide, than makes it working with SiO2, Al2O3 from silica material under hydrothermal condition to generate hydrated calcium silicate. Effective calcium oxide content should be more than 65%, the best is more than 80%.
Aluminum paste ( powder):
Aluminum paste is according to JC/T 407 Aluminum Paste for AAC standard. Aluminum powder should be according to the current national standard.
Gypsum:
The regulating effect of gypsum mainly reflects in deferring the speed of quick lime digesting & slurry thickening.
Water:
According to the standard, water ratio is advisable to 0.60.
Water quality requirement
| Content | pH | Cl- (mg/L) | SO42-(mg/L) | Na+ +K+(mg/L) | K+ (mg/L) |
| Operating range | 6~9 | ＜600 | ＜1000 | ＜450 | ＜100 |